Processes for making cellulose ester compositions

ABSTRACT

A cellulose ester composition is provided comprising at least one cellulose ester and at least one additive selected from the group consisting of a compatibilizer, and a plasticizer. Processes for producing the cellulose ester composition are also provided. In another embodiment, a cellulose ester/elastomer composition is provided comprising at least one elastomer, at least one cellulose ester; and at least one additive; wherein the additive is at least one selected from the group consisting of a compatibilizer and a plasticizer. Processes for producing the cellulose ester/elastomer composition is also provided as well as articles comprising the cellulose ester/elastomer composition.

RELATED APPLICATIONS

This application claims priority from U.S. Provisional Pat. Appln. No. 61/359,582, filed Jun. 29, 2010, the disclosure of which is incorporated herein by reference in its entirety.

FIELD OF THE INVENTION

This invention belongs to the field of cellulose ester chemistry, particularly to cellulose esters comprising compatibilizers and optionally, plasticizers. The invention also belongs to the field of cellulose ester/elastomer compositions comprising at least one elastomer and at least one additive wherein the additive is at least one selected from the group consisting of a compatibilizer and a plasticizer. Processes for producing the cellulose ester compositions and the cellulose ester/elastomer compositions are also provided.

BACKGROUND OF THE INVENTION

This invention relates to the dispersion of cellulose esters in elastomers as small particles to improve the mechanical and physical properties of the elastomer. Polar cellulose esters (CE) are incompatible with non-polar elastomers. In addition, high melting cellulose esters do not melt at typical melt processing temperature of elastomers. These factors make dispersion of cellulose esters into elastomers difficult via most industrially utilized melt mixing process. Due to the above problems, cellulose esters are not an obvious choice as an additive to non-polar elastomers.

This invention can overcome these difficulties by using plasticizers where necessary to help reduce the melt temperature of cellulose esters and by using compatibilizers to help improve mixing and compatibility of cellulose esters and elastomers. Although not wishing to be bound by theory, it is believed that the compatibilizers used can also improve mechanical and physical properties of the cellulose ester/elastomer compositions by improving the interfacial interaction/bonding between the cellulose ester and the elastomer. These cellulose ester/elastomer compositions can be used in rubber/elastomeric applications ranging from tires, hoses, belts, gaskets, automotive parts, and the like.

A process of dispersing cellulose esters in elastomers involves melting or softening cellulose esters so that the cellulose esters can flow and subsequently break down into small particles (dispersion) under shear processing. After dispersion, the cellulose esters can re-solidify upon cooling to room temperature to reinforce the rubber.

BRIEF SUMMARY OF THE INVENTION

In one embodiment of the invention, a cellulose ester composition is provided comprising at least one cellulose ester, at least one compatibilizer, and optionally, and at least one plasticizer.

In another embodiment of the invention, a cellulose ester/elastomer composition is provided comprising at least one elastomer, at least one cellulose ester, and at least one additive; wherein the additive is at least one selected from the group consisting of a compatibilizer and a plasticizer.

In another embodiment of the invention, a process for producing the cellulose ester composition is provided comprising contacting at least one cellulose ester, at least one compatibilizer, and optionally, at least one plasticizer.

In another embodiment of the invention, a process for producing a cellulose ester/elastomer composition is provided comprising mixing at least one elastomer, at least one cellulose ester, and at least one additive for a sufficient time and temperature to disperse the cellulose ester to produce the cellulose ester/elastomer composition; wherein the additive is at least one selected from the group consisting of a compatibilizer and a plasticizer.

DETAILED DESCRIPTION

In one embodiment of the invention, a cellulose ester composition is provided comprising at least one cellulose ester, at least one compatibilizer, and optionally, at least one plasticizer.

The cellulose ester utilized in this invention can be any that is known in the art. The cellulose esters of the present invention generally comprise repeating units of the structure:

wherein R¹, R², and R³ are selected independently from the group consisting of hydrogen or straight chain alkanoyl having from 2 to 10 carbon atoms. For cellulose esters, the substitution level is usually express in terms of degree of substitution (DS), which is the average number of substitutents per anhydroglucose unit (AGU). Generally, conventional cellulose contains three hydroxyl groups in each AGU unit that can be substituted; therefore DS can have a value between zero and three. However, low molecular weight cellulose mixed esters can have a total degree of substitution ranged from about 3.08 to about 3.5. Native cellulose is a large polysaccharide with a degree of polymerization from 700-2,000, and thus the assumption that the maximum DS is 3.0 is approximately correct. However, as the degree of polymerization is lowered, as in low molecular weight cellulose mixed esters, the end groups of the polysaccharide backbone become relatively more significant, thereby resulting in a DS ranging from about 3.08 to about 3.5. Low molecular weight cellulose mixed esters are discussed in more detail subsequently in this disclosure. Because DS is a statistical mean value, a value of 1 does not assure that every AGU has a single substitutent. In some cases, there can be unsubstituted anhydroglucose units, some with two and some with three substitutents, and more often than not the value will be a noninteger. Total DS is defined as the average number of all of substituents per anhydroglucose unit. The degree of substitution per AGU can also refer to a particular substitutent, such as, for example, hydroxyl, acetyl, butyryl, or propionyl.

The cellulose ester utilized can be a cellulose triester or a secondary cellulose ester. Examples of cellulose triesters include, but are not limited to, cellulose triacetate, cellulose tripropionate, or cellulose tributyrate. Examples of secondary cellulose esters include cellulose acetate, cellulose acetate propionate, and cellulose acetate butyrate. These cellulose esters are described in U.S. Pat. Nos. 1,698,049; 1,683,347; 1,880,808; 1,880,560; 1,984,147, 2,129,052; and 3,617,201, incorporated herein by reference in their entirety to the extent that they do not contradict the statements herein.

In one embodiment of the invention, the cellulose esters have at least 2 anhydroglucose rings and typically have between 2 and 5,000 anhydroglucose rings. The number of anhydroglucose units per molecule is defined as the degree of polymerization (DP) of the cellulose ester. Cellulose esters typically have an inherent viscosity (IV) of about 0.2 to about 3.0 deciliters/gram or about 1 to about 1.5, as measured at a temperature of 25° C. for a 0.25 gram sample in 100 ml of a 60/40 by weight solution of phenol/tetrachloroethane. In another embodiment of the invention, the total degree of substitution per anhydroglucose unit (DS/AGU) of the cellulose esters useful herein can range from about 0.5 to about 2.8, from about 1.5 to about 3.0, and from about 1.7 to about 2.7. Examples of cellulose esters include, but are not limited to, cellulose acetate, cellulose propionate, cellulose butyrate, cellulose acetate propionate (CAP), cellulose acetate butyrate (CAB), cellulose propionate butyrate, and the like. Cellulose acetate useful herein typically has a DS/AGU for acetyl of about 2.0 to about 2.5. CAP and CAB typically have a total DS/AGU of about 1.7 to about 2.8.

Cellulose esters can be produced by any method known in the art. Examples of processes for producing cellulose esters are taught in Kirk-Othmer, Encyclopedia of Chemical Technology, 5^(th) Edition, Vol. 5, Wiley-Interscience, New York (2004), pp. 394-444. Cellulose, the starting material for producing cellulose esters, can be obtained in different grades and sources such as from cotton linters, softwood pulp, hardwood pulp, corn fiber and other agricultural sources, and bacterial cellulose, among others.

One method of producing cellulose esters is esterification of the cellulose by mixing cellulose with the appropriate organic acids, acid anhydrides, and catalysts. Cellulose is then converted to a cellulose triester. Ester hydrolysis is then performed by adding a water-acid mixture to the cellulose triester, which can then be filtered to remove any gel particles or fibers. Water is then added to the mixture to precipitate the cellulose ester. The cellulose ester can then be washed with water to remove reaction by-products followed by dewatering and drying.

The cellulose triesters to be hydrolyzed can have three substitutents selected independently from alkanoyls having from 2 to 10 carbon atoms. Examples of cellulose triesters include cellulose triacetate, cellulose tripropionate, and cellulose tributyrate or mixed triesters of cellulose such as cellulose acetate propionate, and cellulose acetate butyrate. These cellulose esters can be prepared by a number of methods known to those skilled in the art. For example, cellulose esters can be prepared by heterogeneous acylation of cellulose in a mixture of carboxylic acid and anhydride in the presence of a catalyst such as H₂SO₄. Cellulose triesters can also be prepared by the homogeneous acylation of cellulose dissolved in an appropriate solvent such as LiCl/DMAc or LiCl/NMP.

Those skilled in the art will understand that the commercial term of cellulose triesters also encompasses cellulose esters that are not completely substituted with acyl groups. For example, cellulose triacetate commercially available from Eastman Chemical Company, Inc., Kingsport, Tenn., U.S.A., typically has a DS from about 2.85 to about 2.95.

After esterification of the cellulose to the triester, part of the acyl substitutents are removed by hydrolysis or by alcoholysis to give a secondary cellulose ester. As noted previously, depending on the particular method employed, the distribution of the acyl substituents can be random or non-random. Secondary cellulose esters can also be prepared directly with no hydrolysis by using a limiting amount of acylating reagent. This process is particularly useful when the reaction is conducted in a solvent that will dissolve cellulose. All of these methods yield cellulose esters that are useful in this invention.

In one embodiment, the secondary cellulose esters useful in the present invention have a weight average molecular weight (Mw) from about 5,000 to about 400,000 as measured by GPC. In a further embodiment, the Mw is from about 10,000 to about 300,000. In yet further embodiments, the Mw ranges from about 10,000 to about 250,000; from about 10,000 to about 100,000, and from about 15,000 to about 80,000.

The most common commercial secondary cellulose esters are prepared by initial acid catalyzed heterogeneous acylation of cellulose to form the cellulose triester. After a homogeneous solution in the corresponding carboxylic acid of the cellulose triester is obtained, the cellulose triester is then subjected to hydrolysis until the desired degree of substitution is obtained. After isolation, a randomly secondary cellulose ester is obtained. That is, the relative degree of substitution (RDS) at each hydroxyl is roughly equal.

In another embodiment of the invention, low molecular weight mixed cellulose esters can be utilized as disclosed in U.S. patent application Ser. No. 10/796,176, herein incorporated by reference to the extent it does not contradict the statements herein. In one embodiment of the invention, the low molecular weight mixed cellulose ester has the following properties: a total degree of substitution per anhydroglucose unit of from about 3.08 to about 3.50, having the following substitutions:

a degree of substitution per anhydroglucose unit of hydroxyl of no more than about 0.70,

a degree of substitution per anhydroglucose unit of C₃-C₄ esters from about 0.80 to about 1.40, and

a degree of substitution per anhydroglucose unit of acetyl of from about 1.20 to about 2.34;

an inherent viscosity of from about 0.05 to about 0.15 dL/g, as measured in a 60/40 (wt./wt.) solution of phenol/tetrachloroethane at 25° C.;

a number average molecular weight (M_(n)) of from about 1,000 to about 5,600;

a weight average molecular weight (M_(w)) of from about 1,500 to about 10,000; and

a polydispersity of from about 1.2 to about 3.5.

In another embodiment of the invention, the low molecular weight cellulose mixed ester has the following properties:

a total degree of substitution per anhydroglucose unit of from about 3.08 to about 3.50, having the following substitutions:

a degree of substitution per anhydroglucose unit of hydroxyl of no more than about 0.70;

a degree of substitution per anhydroglucose unit of C₃-C₄ esters from about 1.40 to about 2.45, and

a degree of substitution per anhydroglucose unit of acetyl of from about 0.20 to about 0.80;

an inherent viscosity of from about 0.05 to about 0.15 dL/g, as measured in a 60/40 (wt./wt.) solution of phenol/tetrachloroethane at 25° C.;

a number average molecular weight (M_(n)) of from about 1,000 to about 5,600;

a weight average molecular weight (M_(w)) of from about 1,500 to about 10,000; and

a polydispersity of from about 1.2 to about 3.5.

In another embodiment of the invention, the low molecular weight cellulose mixed ester has the following properties:

a total degree of substitution per anhydroglucose unit of from about 3.08 to about 3.50, having the following substitutions:

a degree of substitution per anhydroglucose unit of hydroxyl of no more than about 0.70;

a degree of substitution per anhydroglucose unit of C₃-C₄ esters from about 2.11 to about 2.91, and

a degree of substitution per anhydroglucose unit of acetyl of from about 0.10 to about 0.50;

an inherent viscosity of from about 0.05 to about 0.15 dL/g, as measured in a 60/40 (wt./wt.) solution of phenol/tetrachloroethane at 25° C.;

a number average molecular weight (M_(n)) of from about 1,000 to about 5,600;

a weight average molecular weight (M_(w)) of from about 1,500 to about 10,000; and

a polydispersity of from about 1.2 to about 3.5.

The cellulose esters useful in the present invention can be prepared using techniques known in the art and can be commercially obtained, e.g., from Eastman Chemical Company, Kingsport, Tenn., U.S.A.

The cellulose esters utilized in this invention can also contain chemical functionality and are described herein as either derivatized, modified, or functionalized cellulose esters. Functionalized cellulose esters are produced by reacting the free hydroxyl groups of cellulose esters with a bifunctional reactant that has one linking group for grafting to the cellulose ester and one functional group to provide a new chemical group to the cellulose ester. Examples of such bifunctional reactants include succinic anhydride which links through an ester bond and provides acid functionality; mercaptosilanes which links through alkoxysilane bonds and provides mercapto functionality; and isocyanotoethyl methacrylate which links through a urethane bond and gives methacrylate functionality.

In one embodiment of the invention, functionalized cellulose esters are produced by reacting the free hydroxyl groups of the cellulose esters with a bifunctional reactant producing a cellulose ester with at least one functional group selected from the group consisting of unsaturation (double bonds), carboxylic acids, acetoacetate, acetoacetate imide, mercapto, melamine, and long alkyl chains.

Bifunctional reactants to produce cellulose esters containing unsaturation (double bonds) functionality are described in U.S. Pat. Nos. 4,839,230, 5,741,901, 5,871,573, 5,981,738, 4,147,603, 4,758,645, and 4,861,629; all of which are incorporated by reference to the extent they do not contradict the statements herein. In one embodiment, the cellulose esters containing unsaturation is produced by reacting a cellulose ester containing residual hydroxyl groups with an acrylic based compound and m-isopropyenyl-α,α′-dimethylbenzyl isocyanate. The grafted cellulose ester is a urethane-containing product having pendant (meth)acrylate and α-methylstyrene moieties. In another embodiment, the cellulose esters containing unsaturation is produced by reacting maleic anhydride and a cellulose ester in the presence of an alkaline earth metal or ammonium salt of a lower alkyl monocarboxylic acid catalyst, and at least one saturated monocarboxylic acid have 2 to 4 carbon atoms. In another embodiment, the cellulose esters containing unsaturation is produced from the reaction product of (a) at least one cellulosic polymer having isocyanate reactive hydroxyl functionality, and (b) at least one hydroxyl reactive poly(alpha,beta ethyleneically unsaturated) isocyanate.

Bifunctional reactants to produce cellulose esters containing carboxylic acid functionality are described in U.S. Pat. Nos. 5,384,163, 5,723,151, and 4,758,645; all of which are incorporated by reference to the extent they do not contradict the statements herein. In one embodiment, the cellulose esters containing carboxylic acid functionality is produced by reacting a cellulose ester and a mono- or di-ester of maleic or furmaric acid, thereby obtaining a cellulose derivative having double bond functionality. In another embodiment, the cellulose esters containing carboxylic acid functionality has a first and second residue, wherein the first residue is a residue of a cyclic dicarboxylic acid anhydride and the second residue is a residue of an oleophilic monocarboxylic acid and/or a residue of a hydrophilic monocarboxylic acid. In yet another embodiment, the cellulose esters containing carboxylic acid functionality are cellulose acetate phthalates, which can be prepared by reacting cellulose acetate with phthalic anhydride.

Bifunctional reactants to produce cellulose esters containing acetoacetate functionality are described in U.S. Pat. No. 5,292,877; which is incorporated by reference to the extent it does not contradict the statements herein. In one embodiment, the cellulose esters containing acetoacetate functionality are produced by contacting: (i) cellulose; (ii) diketene, an alkyl acetoacetate, 2,2,6, trimethyl-4H 1,3-dioxin-4-one, or a mixture thereof, (iii) a solubilizing amount of solvent system comprising lithium chloride plus a carboxamide selected from the group consisting of 1-methyl-2-pyrrolidinone, N,N dimethylacetamide, or a mixture thereof.

Bifunctional reactants to produce cellulose esters containing acetoacetate imide functionality are described in U.S. Pat. No. 6,369,214 which is incorporated by reference to the extent it does not contradict the statements herein. Cellulose esters containing acetoacetate imide functionality are the reaction product of a cellulose ester and at least one acetoacetyl group and an amine functional compound comprising at least one primary amine.

Bifunctional reactants to produce cellulose esters containing mercapto functionality are described in U.S. Pat. No. 5,082,914; which is incorporated by reference to the extent it does not contradict the statements herein. In one embodiment of the invention, the cellulose ester is grafted with a silicon-containing thiol component which is either commercially available or can be prepared by procedures known in the art. Examples of silicon-containing thiol compounds include, but are not limited to, (3-mercaptopropyl)trimethoxysilane, (3-mercaptopropyl)-dimethyl-methoxysilane, (3-mercaptopropyl)dimethoxymethylsilane, (3-mercaptopropyl)dimethylchlorosilane, (3-mercaptopropyl)dimethylethoxysilane, (3-mercaptopropyl)diethyoxy-methylsilane, and (3-mercapto-propyl)triethoxysilane.

Bifunctional reactants to produce cellulose esters containing melamine functionality are described in U.S. Pat. No. 5,182,379; which is incorporated by reference to the extent it does not contradict the statements herein. In one embodiment, the cellulose esters containing melamine functionality are prepared by reacting a cellulose ester with a melamine compound to form a grafted cellulose ester having melamine moieties grafted to the backbone of the anhydrogluclose rings of the cellulose ester. In one embodiment, the melamine compound is selected from the group consisting of methylol ethers of melamine and aminoplast resins.

Bifunctional reactants to produce cellulose esters containing long alkyl chain functionality are described in U.S. Pat. No. 5,750,677; which is incorporated by reference to the extent it does not contradict the statements herein. In one embodiment, the cellulose esters containing long alkyl chain functionality is produced by reaction of cellulose in a carboxamide diluents or a urea-based diluents with an acylating reagent using a titanium-containing specifies. Cellulose esters containing long alkyl chain functionality can be selected from the group consisting of cellulose acetate hexanoate, cellulose acetate nonanoate, cellulose acetate laurate, cellulose palmitate, cellulose acetate stearate, cellulose nonanoate, cellulose hexanoate, cellulose hexanoate propionate, and cellulose nonanoate propionate.

The plasticizer utilized in this invention can be any that is known in the art that can reduce the melt temperature and/or the melt viscosity of the cellulose ester. The plasticizer can be either monomeric or polymeric in structure. In one embodiment, the plasticizer is at least one selected from the group consisting of a phosphate plasticizer, benzoate plasticizer, adipate plasticizer, a phthalate plasticizer, a glycolic acid ester, a citric acid ester plasticizer and a hydroxyl-functional plasticizer.

In one embodiment of the invention, the plasticizer can be selected from at least one of the following: triphenyl phosphate, tricresyl phosphate, cresyldiphenyl phosphate, octyldiphenyl phosphate, diphenylbiphenyl phosphate, trioctyl phosphate, tributyl phosphate, diethyl phthalate, dimethoxyethyl phthalate, dimethyl phthalate, dioctyl phthalate, dibutyl phthalate, di-2-ethylhexyl phthalate, butylbenzyl phthalate, dibenzyl phthalate, butyl phthalyl butyl glycolate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, triethyl citrate, tri-n-butyl citrate, acetyltriethyl citrate, acetyl-tri-n-butyl citrate, and acetyl-tri-n-(2-ethylhexyl)citrate.

In another embodiment of the invention, the plasticizer can be selected from at least one of the following: esters comprising: (i) acid residues comprising one or more residues of: phthalic acid, adipic acid, trimellitic acid, succinic acid, benzoic acid, azelaic acid, terephthalic acid, isophthalic acid, butyric acid, glutaric acid, citric acid or phosphoric acid; and (ii) alcohol residues comprising one or more residues of an aliphatic, cycloaliphatic, or aromatic alcohol containing up to about 20 carbon atoms.

In another embodiment of the invention, the plasticizer can be selected from at least one of the following: esters comprising: (i) at least one acid residue selected from the group consisting of phthalic acid, adipic acid, trimellitic acid, succinic acid, benzoic acid, azelaic acid, terephthalic acid, isophthalic acid, butyric acid, glutaric acid, citric acid and phosphoric acid; and (ii) at least one alcohol residue selected from the group consisting of aliphatic, cycloaliphatic, and aromatic alcohol containing up to about 20 carbon atoms.

In another embodiment of the invention, the plasticizer can comprise alcohol residues where the alcohol residues is at least one selected from the following: stearyl alcohol, lauryl alcohol, phenol, benzyl alcohol, hydroquinone, catechol, resorcinol, ethylene glycol, neopentyl glycol, 1,4-cyclohexanedimethanol, and diethylene glycol.

In another embodiment of the invention, the plasticizer can be selected from at least one of the following: benzoates, phthalates, phosphates, arylene-bis(diaryl phosphate), and isophthalates. In another embodiment, the plasticizer comprises diethylene glycol dibenzoate, abbreviated herein as “DEGDB”.

In another embodiment of the invention, the plasticizer can be selected from at least one of the following: aliphatic polyesters comprising C₂₋₁₀ diacid residues, for example, malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, and sebacic acid; and C₂₋₁₀ diol residues.

In another embodiment, the plasticizer can comprise diol residues which can be residues of at least one of the following C₂-C₁₀ diols: ethylene glycol, diethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,2-butylene glycol, 1,3-butylene glycol, 1,4-butylene glycol, neopentyl glycol, 1,5-pentanediol, 1,6 hexanediol, 1,5-pentylene glycol, triethylene glycol, and tetraethylene glycol.

In another embodiment of the invention, the plasticizer can include polyglycols, such as, for example, polyethylene glycol, polypropylene glycol, and polybutylene glycol. These can range from low molecular weight dimers and trimers to high molecular weight oligomers and polymers. In one embodiment, the molecular weight of the polyglycol can range from about 200 to about 2000.

In another embodiment of the invention, the plasticizer comprises at least one of the following: Resoflex® R296 plasticizer, Resoflex® 804 plastocizer, SHP (sorbitol hexapropionate), XPP (xylitol pentapropionate), XPA (xylitol pentaacetate), GPP (glucose pentaacetate), GPA (glucose pentapropionate) and APP (arabitol pentapropionate).

In another embodiment of the invention, the plasticizer comprises one or more of: A) from about 5 to about 95 weight % of a C₂-C₁₂ carbohydrate organic ester, wherein the carbohydrate comprises from about 1 to about 3 monosaccharide units; and B) from about 5 to about 95 weight % of a C₂-C₁₂ polyol ester, wherein the polyol is derived from a C₅ or C₆ carbohydrate. In one embodiment, the polyol ester does not comprise or contain a polyol acetate or polyol acetates.

In another embodiment, the plasticizer comprises at least one carbohydrate ester and the carbohydrate portion of the carbohydrate ester is derived from one or more compounds selected from the group consisting of glucose, galactose, mannose, xylose, arabinose, lactose, fructose, sorbose, sucrose, cellobiose, cellotriose and raffinose.

In another embodiment of the invention, the plasticizer comprises at least one carbohydrate ester and the carbohydrate portion of the carbohydrate ester comprises one or more of α-glucose pentaacetate, β-glucosepentaacetate, α-glucose pentapropionate, β-glucose pentapropionate, α-glucose pentabutyrate and β-glucose pentabutyrate.

In another embodiment, the plasticizer comprises at least one carbohydrate ester and the carbohydrate portion of the carbohydrate ester comprises an α-anomer, a β-anomer or a mixture thereof.

In another embodiment of the invention, the plasticizer can be a solid, non-crystalline resin. These resins can contain some amount of aromatic or polar functionality and can lower the melt viscosity of the cellulose esters. In one embodiment of the invention, the plasticizer can be a solid, non-crystalline compound (resin), such as, for example, rosin; hydrogenated rosin; stabilized rosin, and their monofunctional alcohol esters or polyol esters; a modified rosin including, but not limited to, maleic- and phenol-modified rosins and their esters; terpene resins; phenol-modified terpene resins; coumarin-indene resins; phenolic resins; alkylphenol-acetylene resins; and phenol-formaldehyde resins.

The amount of plasticizer in the cellulose ester composition can range from about 1 to about 50 weight percent based on the weight of the cellulose ester. Another range can be from about 5 to about 35 weight percent based on the weight of the cellulose ester.

The compatibilizer can be either a non-reactive compatibilizer or a reactive compatibilizer. The compatibilizer can enhance the ability of the cellulose ester to reach a desired small particle size to improve the dispersion of the cellulose ester into an elastomer. The compatibilizers used can also improve mechanical and physical properties of the cellulose ester/elastomer compositions by improving the interfacial interaction/bonding between the cellulose ester and the elastomer.

When non-reactive compatibilizers are utilized, the compatibilizer contains a first segment that is compatible with the cellulose ester and a second segment that is compatible with a nonpolar elastomer. The first segment contains polar functional groups, which provide compatibility with the cellulose ester, including, but not limited to, such polar functional groups as ethers, esters, amides, alcohols, amines, ketones and acetals. The first segment may consist of oligomers or polymers of the following: cellulose esters; cellulose ethers; polyoxyalkylene, such as, polyoxyethylene, polyoxypropylene, polyoxybutylene; polyglycols, such as, polyethylene glycol, polypropylene glycol, polybutylene glycol; polyesters, such as, polycaprolactone, polylactic acid, aliphatic polyesters, aliphatic-aromatic copolyesters; polyacrylates and polymethacrylates; polyacetals; polyvinylpyrrolidone; polyvinyl acetate; and polyvinyl alcohol. In one embodiment, the first segment is polyoxyethylene or polyvinyl alcohol.

The second segment is compatible with the nonpolar elastomer and contains nonpolar groups. The second segment can be either saturated or unsaturated hydrocarbon groups or contain both saturated and unsaturated hydrocarbon groups. The second segment can be an oligomer or a polymer. In one embodiment of the invention, the second segment of the non-reactive compatibilizer is selected from the group consisting of polyolefins, polydienes, polyaromatics, and copolymers. An example of a polyaromatic second segment is polystyrene. An example of a copolymer second segment is styrene/butadiene copolymer.

The first and second segments of the non-reactive compatibilizers can be in a diblock, triblock, branched or comb structure. The molecular weight of the non-reactive compatibilizers can range from about 300 to about 20,000 or from about 500 to about 10,000 or from about 1,000 to about 5,000. The segment ratio of the non-reactive compatibilizers can range from about 15 to about 85% polar first segments to about 15 to about 85% nonpolar second segments.

Examples of non-reactive compatibilizers include, but are not limited to, ethoxylated alcohols, ethoxylated alkylphenols, ethoxylated fatty acids, block polymers of propylene oxide and ethylene oxide, polyglycerol esters, polysaccharide esters, and sorbitan esters. Examples of ethoxylated alcohols are C₁₁-C₁₅ secondary alcohol ethoxylates, polyoxyethylene cetyl ether, polyoxyethylene stearyl ether, and C₁₂-C₁₄ natural liner alcohol ethoxylated with ethylene oxide. C₁₁-C₁₅ secondary ethyoxylates can be obtained as Dow Tergitol® 15S from the Dow Chemical Company. Polyoxyethlene cetyl ether and polyoxyethylene stearyl ether can be obtained from ICI Surfactants under the Brij® series of products. C₁₂-C₁₄ natural linear alcohol ethoxylated with ethylene oxide can be obtained from Hoechst Celanese under the Genapol® series of products. Examples of ethoxylated alkylphenols include octylphenoxy poly(ethyleneoxy)ethanol and nonylphenoxy poly(ethyleneoxy)ethanol. Octylphenoxy poly(ethyleneoxy)ethanol can be obtained as Igepal® CA series of products from Rhodia, and nonylphenoxy poly(ethyleneoxy)ethanol can be obtained as Igepal CO series of products from Rhodia or as Tergitol® NP from Dow Chemical Company. Ethyoxylated fatty acids include polyethyleneglycol monostearate or monolaruate which can be obtained from Henkel under the Nopalcol® series of products. Block polymers of propylene oxide and ethylene oxide can be obtained under the Pluronic® series of products from BASF. Polyglycerol esters can be obtained from Stepan under the Drewpol® series of products. Polysaccharide esters can be obtained from Henkel under the Glucopon® series of products, which are alkyl polyglucosides. Sorbitan esters can be obtained from ICI under the Tween® series of products.

In another embodiment of the invention, the non-reactive compatibilizers can be synthesized in situ in the cellulose ester composition or the cellulose ester/elastomer composition by reacting cellulose ester-compatible compounds with elastomer-compatible compounds. These compounds can be, for example, telechelic oligomers, which are defined as prepolymers capable of entering into further polymerization or other reaction through their reactive end groups. In one embodiment of the invention, these in situ compatibilizers can have higher molecular weight from about 10,000 to about 1,000,000.

In another embodiment of the invention, the compatibilizer can be reactive. The reactive compatibilizer comprises a polymer or oligomer compatible with one component of the composition and functionality capable of reacting with another component of the composition. There are two types of reactive compatibilizers. The first reactive compatibilizer has a hydrocarbon chain that is compatible with a nonpolar elastomer and also has functionality capable of reacting with the cellulose ester. Such functional groups include, but are not limited to, carboxylic acids, anhydrides, acid chlorides, epoxides, and isocyanates. Specific examples of this type of reactive compatibilizer include, but are not limited to: long chain fatty acids, such as, stearic acid (octadecanoic acid); long chain fatty acid chlorides, such as, stearoyl chloride (octadecanoyl chloride); long chain fatty acid anhydrides, such as, stearic anhydride (octadecanoic anhydride); epoxidized oils and fatty esters; styrene maleic anhydride copolymers; maleic anhydride grafted polypropylene; copolymers of maleic anhydride with olefins and/or acrylic esters, e.g. terpolymers of ethylene, acrylic ester and maleic anhydride; and copolymers of glycidyl methacrylate with olefins and/or acrylic esters, e.g. terpolymers of ethylene, acrylic ester, and glycidyl methacrylate.

Reactive compatibilizers can be obtained as SMA® 3000 styrene maleic anhydride copolymer from Sartomer/Cray Valley, Eastman G-3015® maleic anhydride grafted polypropylene from Eastman Chemical Company, Epolene® E-43 maleic anhydride grafted polypropylene obtained from Westlake Chemical, Lotader® MAH 8200 random terpolymer of ethylene, acrylic ester, and maleic anhydride obtained from Arkema, Lotader® GMA AX 8900 random terpolymer of ethylene, acrylic ester, and glycidyl methacrylate, and Lotarder® GMA AX 8840 random terpolymer of ethylene, acrylic ester, and glycidyl methacrylate.

The second type of reactive compatibilizer has a polar chain that is compatible with the cellulose ester and also has functionality capable of reacting with a nonpolar elastomer. Examples of these types of reactive compatibilizers include cellulose esters or polyethylene glycols with olefin or thiol functionality. Reactive polyethylene glycol compatibilizers with olefin functionality include, but are not limited to, polyethylene glycol allyl ether and polyethylene glycol acrylate. An example of a reactive polyethylene glycol compatibilizer with thiol functionality includes polyethylene glycol thiol. An example of a reactive cellulose ester compatibilizer includes mercaptoacetate cellulose ester.

The amount of compatibilizer in the cellulose ester composition can range from about 1 wt % to about 40 wt % or from about 5 wt % to about 20 wt % based on the weight of the cellulose ester.

In another embodiment of this invention, a cellulose ester/elastomer composition is provided comprising at least one elastomer, at least one cellulose ester, and at least one additive; wherein the additive is at least one selected from the group consisting of at least one plasticizer and at least one compatibilizer. The cellulose esters, plasticizers, and compatibilizers have been previously described in this disclosure. The elastomer in this invention is at least one non-polar elastomer known in the art. In one embodiment, the non-polar elastomer is primarily based on hydrocarbon. For example, non-polar elastomers include, but are not limited to, natural rubber, polybutadiene, polyisoprene, styrene-butadiene rubber, polyolefins, ethylene propylene diene monomer (EPDM), and polynorbornene. Examples of polyolefins include, but are not limited to, polybutylene, polyisobutylene, and ethylene propylene rubber.

The amount of cellulose ester in the cellulose ester/elastomer composition ranges from about 1 to about 50 parts per hundred rubber (phr) based on the elastomer. Other ranges are from about 5 to about 30 phr and about 3 to about 30 phr based on the weight of the elastomer.

The amount of compatibilizer can range from about 1% to about 40% by weight based on the weight of the cellulose ester. Another range is from about 5 to about 20% by weight based on the weight of the cellulose ester.

The amount of plasticizer can range from about 1% to about 50% by weight based on the weight of the cellulose ester. Another range is from about 5% to about 35% by weight based on the weight of the cellulose ester.

In another embodiment of the invention, the cellulose ester/elastomer compositions further comprise at least one crosslinking/curing agent. Crosslinking/curing agents can be any that is known in the art. Examples of crosslinking/curing agents include, but are not limited to, organic peroxides and sulfur.

In another embodiment of the invention, a process for producing a cellulose ester composition is provided. The process comprises contacting at least one cellulose ester, at least one compatibilizer, and optionally, at least one plasticizer. The cellulose ester, plasticizer, and compatibilizer were previously discussed in this disclosure. The cellulose ester, compatibilizer, and optional plasticizer can be mixed in any order of addition.

In another embodiment of this invention, a process for producing a cellulose ester/elastomer composition is provided comprising: a) mixing at least one elastomer, at least one cellulose ester, and at least one additive for a sufficient time and temperature to disperse the cellulose ester to produce the cellulose ester/elastomer composition; wherein the additive is at least one selected from the group consisting of a compatibilizer and a plasticizer. A sufficient temperature is defined as the flow temperature of the cellulose ester which is generally about 50° C. above the Tg of the cellulose ester. The temperature at mixing is limited at the upper range by the processing temperature of the elastomer and at the lower range by the highest use temperature of the cellulose ester/elastomer composition.

It is known in the art that the efficiency of mixing two or more viscoelastic materials can depend on the ratio of the viscosities of the viscoelastic materials. For a given mixing equipment and shear rate range, the viscosity ratio of the dispersed phase (cellulose ester and additive) and continuous phase (elastomer) should be within specified limits for obtaining adequate particle size. In one embodiment of the invention where low shear rotational shearing equipment is utilized, such as, Banbury and Brabender mixers, the viscosity ratio of the dispersed phase (cellulose ester and additive) to the continuous phase (elastomer) can range from about 0.001 to about 5, from about 0.01 to about 5, and from about 0.1 to about 3. In yet another embodiment of the invention where high shear rotational/extensional shearing equipment is utilized, such as, twin screw extruders, the viscosity ratio of the dispersed phase (cellulose ester and additive) to the continuous phase (elastomer) can range from about 0.001 to about 500 and from about 0.01 to about 100.

It is also known in the art that when mixing two or more viscoelastic materials, the difference between the interfacial energy of the two viscoelastic materials can affect the efficiency of mixing. Mixing can be more efficient when the difference in the interfacial energy between the materials are less.

In one embodiment of the invention, the surface tension difference between the dispersed phase (cellulose ester and additive) and continuous phase (elastomer) is less than about 100 dynes/cm, less than 50 dynes/cm, or less than 20 dynes/cm.

In one embodiment, the cellulose ester is softened and/or melted to allow breakdown of the cellulose ester into sufficiently small particle size under the specified mixing conditions. In one embodiment, the particle size of the cellulose ester can be between 50 microns to 50 nanometers. In one embodiment of the invention, the elastomer, at least one cellulose ester, and at least one additive are contacted at a temperature in the range of about 70° C. to about 220° C. or from about 100° C. to about 180° C., or from about 130° C. to about 160° C.

Mixing of the elastomer, cellulose ester, and additive can be accomplished by any method known in the art that is adequate to disperse the additive. Examples of mixing equipment include, but are not limited to, Banbury mixers, Brabender mixers, and extruders (single or twin screw). The shear energy during the mixing is dependent on the combination of equipment, blade design, rotation speed (rpm), and mixing time. The shear energy should be sufficient for breaking down softened/melted cellulose ester to a small enough size to disperse the cellulose ester throughout the elastomer. For example, when a Banbury mixer is utilized, the shear energy and time of mixing ranges from about 5 to about 15 minutes at 100 rpms.

The elastomer, cellulose ester and additive can be combined in any order during the process. In one embodiment, the cellulose ester is premixed with the compatibilizer and/or the plasticizer. The cellulose ester containing the compatibilizer and/or the plasticizer is then mixed with the elastomer. In another embodiment of the invention, when reactive compatibilizers are utilized, the reactive compatibilizers can be mixed with either the cellulose ester or the elastomer first, then the other components are added.

In another embodiment of the invention, a process to produce a cellulose ester/elastomer compositions comprising: a) mixing at least one elastomer, at least one cellulose ester and at least one additive for a sufficient time and temperature to disperse the cellulose ester throughout said elastomer to produce a cellulose ester/elastomer masterbatch; wherein the additive is at least one selected from the group consisting of a compatibilizer and a plasticizer; and b) mixing the masterbatch and at least one elastomer to produce the cellulose ester/elastomer composition. The elastomer in the masterbatch can be the same or different than that utilized to produce the cellulose ester/elastomer composition. The processes of mixing have been previously discussed in this disclosure.

This invention can be further illustrated by the following examples of preferred embodiments thereof, although it will be understood that these examples are included merely for purposes of illustration and are not intended to limit the scope of the invention unless otherwise specifically indicated.

EXAMPLES Example 1 Non-Reactive Compatibilizer in Cellulose Ester/Elastomer Compositions

Experiments were conducted to evaluate certain non-reactive compatibilizer in cellulose ester/elastomer compositions. In Table 1, the non-reactive compatibilizers evaluated are listed.

TABLE 1 Compatibilizer Compound MW¹ #CH₂ ² #EO³ % EO MP⁴ ° C. Tergitol 15-S-9 570 15 9 63 <RT Tergitol 15-S-30 1400 15 30 85 ~50 Polyethylene 920 32 12 50 ~100 block polyethylene glycol⁵ Polyethylene 2250 32 40 80 ~85 block polyethylene glycol Polyethylene 1400 50 16 50 ~100 block polyethylene glycol ¹Molecular Weight ²Number of carbon atoms ³Number of Ethylene Oxide groups ⁴Melting Point ⁵PE Block PEG

Tergitol 15-S-9 and Tergitol 15-S-30 are secondary alcohol ethoxylates obtained from Dow Chemical in Midland, Mich. The polyethylene block polyethylene glycol compatibilizers were obtained from Sigma-Aldrich. Although not wishing to be bound by theory, it is believed that the ethylene oxide units of the above compounds plasticizes the cellulose acetate butyrate and the hydrocarbon chain improves compatibility with the elastomer. Each of the compatibilizers was blended with cellulose acetate butyrate (CAB 551-0.01 and CAB 553.0.4) obtained from Eastman Chemical Company, Kingsport, Tenn. at 80:20 ratio in a Brabender mixer at 150° C. for 10 minutes at 100 rpm) followed by cryogrinding to prepare the masterbatches of cellulose ester and compatibilizer (MB 1-10) as shown in Table 2.

TABLE 2 CAB CAB PE PE PE Master 551- 553- Tergitol Tergitol Block Block Block Batch 0.01 0.4 15-S-9 15-S-30 PEG PEG PEG Tg, ° C. MB 1 80 20 49.3 MB 2 80 20 52.6 MB 3 80 20 54.3 MB 4 80 20 66.6 MB 5 80 20 97.5 MB 6 80 20 82.3 MB 7 80 20 75.8 MB 8 80 20 84.2 MB 9 80 20 69.5 MB 10 80 20 104.7 Reference Tg for CAB 551-0.01 is 107° C. and for CAB 553-0.4 is 139° C. All the above master batches of cellulose ester and compatibilizer are compounded with a non-oil modified solution styrene-butadiene rubber obtained as Duradene 761 from Firestone Polymers, Akron, Ohio, using the procedure outlined subsequently in these Examples to prepare sample compositions shown in Table 3.

TABLE 3 CAB CAB Comp Duradene 551- 553- MB MB MB MB MB MB MB MB MB MB No. 761 0.01 0.4 1 2 3 4 5 6 7 8 9 10 1.1 100 1.2 100 10 1.3 100 12.5 1.4 100 12.5 1.5 100 12.5 1.6 100 12.5 1.7 100 12.5 1.8 100 10 1.9 100 12.5 1.10 100 12.5 1.11 100 12.5 1.12 100 12.5 1.13 100 12.5 The amounts specified in Table 3 are based on 100 grams of rubber and expressed as parts per hundred rubber (phr). For example, for Composition 1.3, 100 grams of rubber was utilized as well as 12.5 grams of Masterbatch 1, which is an 80:20 ratio of cellulose acetate butyrate (CAB 553-0.4) and Tergitol 15-S-9 secondary alcohol ethoxylate.

All cellulose ester, elastomer, and compatibilizers in Table 3 were processed in a Brabender mixer for 30 minutes at 150° C. and 100 rpm to produce the cellulose ester/elastomer composition. Then, 2.5 phr dicumyl peroxide (curing agent) was added to each sample at 50-60° C. in a Brabender mixer for about 1 minute and then mixed for another 2-3 minutes to produce a partially cured cellulose ester/elastomer composition. The samples from the Brabender mixer were cured by compression molding for 45 minutes at 150° C. and 20000 psi.

The modulus, yield stress, and yield strain of the compression molded, cured cellulose ester/elastomer composition samples were measured as per ASTM D412 and are shown in Table 4. In the ASTM D412 method, samples were prepared by cutting the specimens with Die C. The speed of testing was 20 inches/min, and the gauge length was 63.5 mm (2.5 inch). The samples were conditioned in the laboratory for 40 hours at 50%+/−5% humidity and 72° F. The width of the specimen was 1 inch and the length was 4.5 inches.

TABLE 4 Composition Modulus, Yield Stress, Number MPa MPa Yield Strain, % 1.1 6.99 1.37 22.11 1.2 7.75 1.66 22.44 1.3 8.29 1.67 24.41 1.4 8.61 1.91 26.67 1.5 7.87 1.86 28.23 1.6 9.57 2.03 26.76 1.7 9.53 1.98 24.73 1.8 10.77 1.27 12.93 1.9 10.14 1.45 16.8 1.10 7.46 1.62 25.88 1.11 6.44 1.16 21.42 1.12 9.08 1.53 20.02 1.13 10.61 1.63 17.33 In Compositions 1.3-1.7, the addition of the compatibilizer to the elastomer and cellulose ester showed an improvement in modulus, yield stress, and yield strain over the Comparative Compositions 1.1 and 1.2 containing either rubber alone or rubber and cellulose ester alone. In Compositions 1.9-1.13, the Yield Strain and Yield Stress were improved over the Comparative Composition 1.8.

Example 2 Reactive Compatabilizers in Cellulose Ester/Elastomer Compositions

Reactive compatibilizers were evaluated to improve the mixing of CAB in styrene butadiene rubber (SBR). The reactive compatibilizers were selected such that they contained reactive groups that can react with the CAB and the rest of the molecule is compatible with the SBR. The molecular weight, and the type and concentration of the reactive moiety were varied.

TABLE 5 Brand Chemical Reactive Acid number, Name Composition Manufacturer Moiety Mw mg KOH/gm Tm, ° C. Comments SMA Styrene Sartomer/Cray Maleic 9500 285 180 Styrene: 3000 maleic Valley anhydride (Tm ~ MA = 3:1 anhydride Tg + copolymer 55) Eastman Maleic Eastman Maleic 47000 15 156 G-3015 anhydride anhydride grafted polypropylene Epolene Maleic Westlake Maleic 15800 45 158 E-43 anhydride Chemicals anhydride grafted polypropylene Lotader Random Arkema Maleic 17 100 Maleic MAH terpolymer of anhydride anhydride 8200 Ethylene, ~2.8 wt % Acrylic ester Ester and Maleic ~6.5 wt % anhydride Lotader Random Arkema Glycidyl NA 65 Glycidyl GMA AX terpolymer of Methacrylate Methacrylate 8900 Ethylene, (epoxy)   ~8 wt %, Acrylic ester Ester and glycidyl  ~25 wt % Methacrylate Lotader Random Arkema Glycidyl NA 106 Glycidyl GMA AX terpolymer of Methacrylate Methacrylate 8840 Ethylene, (epoxy)   ~8 wt %, Acrylic ester Ester and glycidyl   ~0 wt % Methacrylate

The maleic anhydride and glycidyl methacrylate in these reactive compatibilizers can react with the hydroxyl group contained in the cellulose ester. Masterbatches of Duradene 761 styrene butadiene rubber and a reactive compatibilizer were produced as shown in Table 6. Duradene 761 styrene butadiene rubber and the reactive compatibilizer were mixed in a Brabender mixer at 100 rpm and 160° C. for 30 minutes to produce the masterbatches (MB1-MB6).

TABLE 6 Composition Duradene 761, Compatibilizer No. gm Compatibilizer quantity, gm MB 1 100 SMA 3000 3 MB 2 100 Eastman G-3015 3 MB 3 100 Epolene E-43 3 MB 4 100 Lotader MAH 8200 3 MB 5 100 Lotader GMA AX 8900 3 MB 6 100 Lotader GMA AX 8840 3 The cellulose ester/elastomer compositions produced are shown in Table 7. Composition Number 2.1 contained only SBR. Composition Number 2.2 contained only SBR and CAB 551-0.01. For Composition Numbers 2.3-2.8, the masterbatches produced containing SBR and compatibilizer were mixed with cellulose ester in a Brabender mixer at 100 rpm for 30 minutes at 150° C.

A CAB/plasticizer masterbatch was prepared by blending 100 g CAB 553-0.4 and 10 g Eastman 168 plasticizer (bis(2-ethylhexyl)-1,4-benzenedicarboxylate) obtained from Eastman Chemical Company using a Brabender mixer at 100 rpm and 150° C. for 10 minutes. The CAB/plasticizer masterbatch was cryo-ground to a powder. Eastman 168 plasticizer was added to reduce the Tg/Tm of the CAB 553-0.4 so that it melted at a processing temperature of about 150° C. The Tg of the CAB/plasticizer masterbatch was obtained by preparing samples dissolved in acetone followed by vacuum drying at 70° C. and analyzing the samples by Differential Scanning calorimetry (DSC) (2nd cycle). Only CAB 553-0.4 was utilized in the masterbatches. CAB 551-0.01 was mixed with Eastman 168 plasticizer to determine the Tg. The glass transition temperatures (Tg) of the cellulose ester/plasticizer compositions produced are shown in Table 8.

TABLE 7 CAB MB Composition Duradene 551- (CAB/ MB MB MB MB MB MB Number 761 0.01 Plasticizer) 1 2 3 4 5 6 2.1 100 2.2 100 10 2.3 10 103 2.4 10 103 2.5 10 103 2.6 10 103 2.7 10 103 2.8 10 103 2.9 100 11 2.10 11 103 2.11 11 103 2.12 11 103 2.13 11 103 2.14 11 103 2.15 11 103

TABLE 8 Plasticizer wt % Tg, ° C. CAB 551-0.01 (10 g) + Plasticizer 168 (0.5 g) 5 90.5 CAB 551-0.01 (10 g) + Plasticizer 168 (1.0 g) 10 75.5 CAB 553-0.4 (10 g) + Plasticizer 168 (0.5 g) 5 123.7 CAB 553-0.4 (10 g) + Plasticizer 168 (1.0 g) 10 109.5

Once the masterbatches were prepared, the CAB 551-0.01 and the CAB/Plasticizer Masterbatch were dried overnight at 50° C. to remove moisture before blending. Composition Numbers 2.1-2.15 were prepared by weighing each component in Table 6 separately and processing the components in a Brabender mixed at 100 rpm for 30 minutes at 150° C. In order to cure the cellulose ester/elastomer composition, 1 g of dicumyl peroxide (i.e. 2.5 phr) was added to the Brabender mixer over a period of about 1 minute and then the composition was further mixed for another 2-3 minutes to produce a partially cured cellulose ester/elastomer composition. The curing of the cellulose ester/elastomer composition was then completed by compression molding for 45 minutes at 150° C. and 20000 psi.

The modulus, yield stress and yield strain of the compression molded cured samples were measured as per ASTM D412 and are shown in Table 9.

TABLE 9 Composition Modulus, Yield Stress, Number MPa MPa Yield Strain, % 2.1 6.99 1.37 22.11 2.2 7.66 1.45 21.66 2.3 14.08 2.01 18.05 2.4 10.55 1.73 17.62 2.5 7.01 1.45 23.27 2.6 14.65 1.79 13.66 2.7 9.89 1.69 20.00 2.8 11.36 2.2 22.62 2.9 10.48 1.39 14.52 2.10 11.82 1.69 15.23 2.11 9.89 1.72 18.68 2.12 8.92 1.68 20.49 2.13 8.95 1.53 18.49 2.14 6.82 1.32 23.19 2.15 7.35 1.56 25.23 These data show that the addition of CAB 551-0.01 to a masterbatch of rubber and a reactive compatibilizer in Compositions 2.3-2.8 showed an increase in modulus over Comparative Composition 2.1 with rubber alone or Composition 2.2 with rubber and CAB 551-0.01. Yield Strain and to some extent Yield Stress was also improved in Compositions 2.10-2.15 in comparison to Composition 2.9 when the CAB/Plasticizer masterbatch was added to the SBR/Compatibilizer masterbatch.

Example 3 Use of Plasticizers

Masterbatches of cellulose esters with two different plasticizers at various loadings were prepared in an attempt to lower the Tg of the cellulose esters such that their flow temperature is lower than the typical rubber processing temperature of 150° C. Compounding in a Brabender mixer at 150° C. for 10 minutes at 100 rpm followed by cryogrinding yielded the masterbatches shown in Table 10.

TABLE 10 Quan- Quantity Tg of Tg of tity of master Master CE, of CE, Type of plasticizer, Batch, Batch CE¹ ° C. g Plasticizer g ° C. MB 1 CAB 101 100 Eastman 168² 10 84 551-0.2 MB 2 CAB 136 100 Eastman 168 25 85 553-0.4 MB 3 CAB 123 100 Eastman 168 20 87 381-0.1 MB 4 CAB 133 100 Eastman 168 25 95 381-2 MB 5 CAB 136 100 Poly (ethylene 25 65 553-0.4 glycol)³ MB 6 CAB 133 100 Poly (ethylene 25 70 381-2 glycol) MB 7 CAP 159 100 Poly (ethylene 30 93 504-0.2 glycol) MB 8 CAP 142 100 Poly (ethylene 25 90 482-0.5 glycol) MB 9 CA 180 100 Poly (ethylene 40 109 398-3 glycol) ¹CE—Cellulose Ester ²bis(2-ethylhexyl)-1,4-benzene dicarboxylate ³polyethylene glycol - molecular weight 300 - from Aldrich All the above masterbatches were compounded with styrene butadiene rubber (SBR). The SBR and the masterbatch were mixed in a Brabender mixer for 30 minutes at 150° C. and 100 rpm. 2.5 phr dicumyl peroxide (curing agent) were added to each sample at 50-60° C. in the Brabender mixer in 1 minute and then mixed for another 2-3 minutes. The samples from the Brabender mixer were compression molded for 45 minutes at 150° C. and 20000 psi. The formulation of these samples are shown in Table 11. Each cellulose ester containing masterbatch sample has 10 phr (parts per hundred rubber) cellulose ester.

TABLE 11 Composition No. CE CE Quantity, g Duradene 761, g 3.1 None 100 3.2 MB 1 11 100 3.3 MB 2 12.5 100 3.4 MB 3 12 100 3.5 MB 4 12.5 100 3.6 MB 5 12.5 100 3.7 MB 6 12.5 100 3.8 MB 7 13 100 3.9 MB 8 12.5 100 3.10 MB 9 14 100 comparative? The modulus, yield stress and yield strain of the compression molded, cured, elastomer/cellulose ester composition samples were measured as per ASTM D412 and are shown in Table 12.

TABLE 12 Composition Modulus, Yield Stress, Number MPa MPa Yield Strain, % 3.1 6.99 1.37 22.11 3.2 7.47 1.26 19.25 3.3 7.32 1.29 20.45 3.4 12.12 1.83 17.29 3.5 13.45 1.84 14.8 3.6 11.47 1.89 17.99 3.7 13.36 2.07 17.93 3.8 8.43 1.37 18.57 3.9 11.36 1.54 14.83 3.10 10.67 1.44 15.92 These data show that for Composition Numbers 3.2-3.11, the modulus was improved over Comparative Composition 3.1.

Example 4 Use of Cellulose Esters and Plasticizers in Tire Formulations

This example is provided to show the advantages of the use of cellulose esters with plasticizers in tire formulations over cellulose esters alone. Table 13 shows the tire formulations. All amounts in Table 13 are based on parts per hundred rubber (phr). Table 14 shows the cellulose ester/plasticizer masterbatch formulations.

Table 15 shows the mixing conditions. The components were mixed in a Banbury mixer, which was a Farrel BR mixer with steam heating and water cooling which is instrumented with computer monitors for temperature, rpm, and power. After preparing the elastomer/cellulose ester/plasticizer composition, the composition was cured T₉₀+5 minutes at 320° F. (160° C.).

TABLE 13 Formulations of Cellulose Ester - Filled Tire Tread Ingredients Sample Name CAB-1 CAB-2 CAB-3 Stage 1 Buna VSL 5025-2¹ S-SBR, 37.5phr 103.12 103.12 103.12 TDAE² Buna CB24³ PBD rubber 25 25 25 Rhodia 1165 MP Silica 70 70 70 Si69⁴ Coupling agent 5.47 5.47 5.47 Sundex 790⁵ Aromatic Oil 5 5 5 Stearic acid Cure Activator 1.5 1.5 1.5 Stage 2 Product of stage 1 210.09 210.09 210.09 Cellulose Ester MB-1 10 MB⁶ MB-2 12.5 MB-3 12.5 Zinc oxide Cure activator 1.9 1.9 1.9 Okerin ® wax 7240⁷ microcrystalline 1.5 1.5 1.5 wax Santoflex ® 6PPD⁸ Anti-oxidant 2 2 2 KK49⁹ process aid 2 2 2 Stage 3 Product of stage 2 217.49 229.99 229.99 Sulfur Cross-linker 1.5 1.5 1.5 Santocure ® CBS¹⁰ Accelerator 1.3 1.3 1.3 Perkacit ® DPG- Accelerator 1.5 1.5 1.5 grs¹¹ Total 221.79 234.29 234.29 Compounds ¹S-SBR—solution styrene butadiene rubber obtained from Lanxess. ²TDAE—treated distillate aromatic extract ³PBD—polybutadiene rubber obtained from Lanxess ⁴Si69 is a sulfur-containing organosilane obtained from Arkema ⁵Sundex ® 790 is an aromatic oil obtained from Sunoco ⁶MB—Masterbatch ⁷Okerin wax 7240 is a microcrystalline wax obtained from Sovereign Chemical ⁸Santoflex 6PPD is an anti-oxidant obtained from Flexsys. ⁹KK49 is a processing aid obtained from Strutkol. ¹⁰Santocure CBS is an accelerator obtained from Flexsys. ¹¹Perkacit DPG-grs is an accelerator obtained from Flexsys.

TABLE 14 Compositions of Plasticized Cellulose Ester Masterbatches PHR of MB Tg before Plasticizer Pz level in Tg after MB-Y CE Plasticizer, C (Pz) (g/100 g CE) formulation plasticizer, C MB-1 CAB 381-2 133 None — 10 133 MB-2 CAB 381-2 133 EMN 168¹ 25 12.5 95 MB-3 CAB 381-2 133 PEG-300² 25 12.5 70

TABLE 15 Processing of Cellulose-Ester Filled Tire Tread Compounds in a Banbury Mixer Mix conditions Stage 1 mix conditions Start temperature 65° C. Starting rotor speed, rpm 65 Fill factor 67% Mix sequence at 0 minute add elastomers at 1 minute add ⅔ silica + Si69 at 2 minute add ⅓ silica + others at 3 minute sweep at 3.5 minute increase rotor speed to ramp temperature to 160° C. in 4.5 minutes Dump Condition hold 2 minutes at 160° C. (Total mix time = 6.5 minutes) Stage 2 mix conditions Start temperature 65° C. Starting rotor speed, rpm 65 Fill factor 64% Mix sequence at 0 minute add ½ of first pass batch at 15 second add other ingredients in a pocket and ½ of first pass batch at 1 minute sweep at 1.5 minute increase rotor speed to ramp temperature to 140-145° C. in 3.5 minutes Dump Condition Hold 4 minutes at 140-145° C. (total mix time = 7.5 minutes) Stage 3 mix conditions Start temperature 50° C. Starting rotor speed, rpm 60 Fill factor 61% Addition order at 0 minute add ½ 2nd pass batch, at 15 second add sulfur, accelerators and ½ 2nd pass batch, sweep at 1 minute. Dump conditions 110° C. or 2 minute 30 second

TABLE 16 Performance of Cellulose Ester-Filled Tire Tread Compounds CAB-2 CAB-3 CAB-1 CAB 381-2 + CAB 381-2 + Properties CAB 381-2 25 phc E168 25 phc PEG Compounding Mooney viscosity, 4 63.5 58.5 55.1 minute at 100° C. Cured Rubber Phillips Dispersion 1 4 4 Break stress, psi 2191 2240 2349 Break strain, % 386 387 366 Modulus(M100), psi 663 679 735 Modulus (M300), 1693 1723 1918 psi Shore A Hardness 61 59 62 Tan Delta 0° C. 0.306 0.292 0.313 Tan Delta 60° C. 0.082 0.081 0.076 Rebound 0° C., % 9.8 10.8 9.6 Rebound 60° C., % 62.2 62.8 64.0 Wear, volume loss 136 124 127 in mm³

Performance Measurement:

Descriptions of various analytical techniques used to measure performance are provided below:

-   -   Mooney Viscosity: The Mooney Viscosities were measured according         to ASTM D 1646.     -   PHILLIPS Dispersion Rating: The samples were cut with a razor         blade, and pictures were taken at 30× magnification with an         Olympus SZ60 Zoom Stereo Microscope interfaced with a PaxCam ARC         digital camera and a Hewlett Packard 4600 LaserJet color         printer. The pictures of the samples were then compared to a         Phillips standard dispersion-rating chart having standards         ranging from 1 (bad) to 10 (excellent).     -   Mechanical Properties: Break stress, break strain, modulus at         100%, and 300% strains were measured as per ASTM D412 using Die         C for specimen preparation. The speed of testing was 20         inches/min, and the gauge length was 63.5 mm (2.5 inch). The         samples were conditioned in the lab for 40 hours at 50%+/−5%         humidity and 72° F. The width of specimen was 1 inch, and length         was 4.5 inch.     -   Hardness: Shore A hardness was measured according to ASTM D2240.

Dynamic Mechanical Analysis:

-   -   -   Temperature Sweep: A TA instruments Dynamic Mechanical             Analyzer was used to complete the temperature sweeps using a             tensile geometry. Storage modulus (E′), Loss modulus (E″),             and tan delta (=E″/E′) were measured as a function of             temperature from −80° C. to 120° C. using 10 Hz frequency,             and 5% static and 0.2% dynamic strain.

    -   Rebound Test: The rebound pendulum test was carried out as per         ASTM D7121-05.

    -   Wear: Din abrasion testing was performed per ASTM 222.         The data show that without the use of a plasticizer, the         cellulose ester did not disperse as well through the elastomer         as shown by the poor Phillips Dispersion data. Further, the         Mooney viscosities of the compositions containing both cellulose         ester and plasticizer were lower than when plasticizer was not         utilized. This shows that in the presence of the plasticizer,         CEs acted as a processing aid and lowered Mooney viscosity.         Furthermore, the break stress and wear was also improved over         compositions without plasticizer, presumably indicating that in         presence of the plasticizers, CEs can disperse into finer         particles and can improve the properties that are dependent on         particle size and/or surface area. 

1. A cellulose ester/elastomer composition comprising at least one cellulose ester, at least one elastomer, and at least one additive selected from the group consisting of a compatibilizer, and a plasticizer.
 2. The cellulose ester/elastomer composition according to claim 1 wherein said cellulose ester has an inherent viscosity (IV) of about 0.2 to about 3.0 deciliters/gram.
 3. The cellulose ester/elastomer composition according to claim 1 wherein said cellulose ester has a total degree of substitution per anhydroglucose unit (DS/AGU) from about 0.5 to about 2.8.
 4. The cellulose ester/elastomer composition according to claim 1 wherein the cellulose ester is a low molecular weight cellulose mixed ester selected from the group consisting of: a) a low molecular weight mixed cellulose ester having the following properties: a total degree of substitution per anhydroglucose unit of from about 3.08 to about 3.50, having the following substitutions: a degree of substitution per anhydroglucose unit of hydroxyl of no more than about 0.70, a degree of substitution per anhydroglucose unit of C₃-C₄ esters from about 0.80 to about 1.40, and a degree of substitution per anhydroglucose unit of acetyl of from about 1.20 to about 2.34; an inherent viscosity of from about 0.05 to about 0.15 dL/g, as measured in a 60/40 (wt./wt.) solution of phenol/tetrachloroethane at 25° C.; a number average molecular weight (M_(n)) of from about 1,000 to about 5,600; a weight average molecular weight (M_(w)) of from about 1,500 to about 10,000; and a polydispersity of from about 1.2 to about 3.5; and b) a low molecular weight mixed cellulose ester having the following properties: a total degree of substitution per anhydroglucose unit of from about 3.08 to about 3.50, having the following substitutions: a degree of substitution per anhydroglucose unit of hydroxyl of no more than about 0.70; a degree of substitution per anhydroglucose unit of C₃-C₄ esters from about 1.40 to about 2.45, and a degree of substitution per anhydroglucose unit of acetyl of from about 0.20 to about 0.80; an inherent viscosity of from about 0.05 to about 0.15 dL/g, as measured in a 60/40 (wt./wt.) solution of phenol/tetrachloroethane at 25° C.; a number average molecular weight (M_(n)) of from about 1,000 to about 5,600; a weight average molecular weight (M_(w)) of from about 1,500 to about 10,000; and a polydispersity of from about 1.2 to about 3.5; and c) a low molecular weight mixed cellulose ester having the following properties: a total degree of substitution per anhydroglucose unit of from about 3.08 to about 3.50, having the following substitutions: a degree of substitution per anhydroglucose unit of hydroxyl of no more than about 0.70; a degree of substitution per anhydroglucose unit of C₃-C₄ esters from about 2.11 to about 2.91, and a degree of substitution per anhydroglucose unit of acetyl of from about 0.10 to about 0.50; an inherent viscosity of from about 0.05 to about 0.15 dL/g, as measured in a 60/40 (wt./wt.) solution of phenol/tetrachloroethane at 25° C.; a number average molecular weight (M_(n)) of from about 1,000 to about 5,600; a weight average molecular weight (M_(w)) of from about 1,500 to about 10,000; and a polydispersity of from about 1.2 to about 3.5.
 5. The cellulose ester/elastomer composition according to claim 1 wherein said cellulose ester is a functionalized cellulose ester wherein said functionalized cellulose ester is functionalized by at least one bifunctional reactant producing a cellulose ester with at least one functional group selected from the group consisting of unsaturation (double bonds), carboxylic acids, acetoacetate, acetoacetate imide, mercapto, melamine, and long alkyl chains.
 6. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer is at least one selected from the group consisting of a phosphate plasticizer, benzoate plasticizer, adipate plasticizer, a phthalate plasticizer, a glycolic acid ester, a citric acid ester plasticizer and a hydroxyl-functional plasticizer.
 7. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer is at least one selected from the group consisting of triphenyl phosphate, tricresyl phosphate, cresyldiphenyl phosphate, octyldiphenyl phosphate, diphenylbiphenyl phosphate, trioctyl phosphate, tributyl phosphate, diethyl phthalate, dimethoxyethyl phthalate, dimethyl phthalate, dioctyl phthalate, dibutyl phthalate, di-2-ethylhexyl phthalate, butylbenzyl phthalate, dibenzyl phthalate, butyl phthalyl butyl glycolate, ethyl phthalyl ethyl glycolate, methyl phthalyl ethyl glycolate, triethyl citrate, tri-n-butyl citrate, acetyltriethyl citrate, acetyl-tri-n-butyl citrate, and acetyl-tri-n-(2-ethylhexyl)citrate.
 8. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer is selected from at least one of the following: esters comprising: (i) acid residues comprising one or more residues of: phthalic acid, adipic acid, trimellitic acid, succinic acid, benzoic acid, azelaic acid, terephthalic acid, isophthalic acid, butyric acid, glutaric acid, citric acid or phosphoric acid; and (ii) alcohol residues comprising one or more residues of an aliphatic, cycloaliphatic, or aromatic alcohol containing up to about 20 carbon atoms.
 9. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer comprises alcohol residues where the alcohol residues is at least one selected from the following: stearyl alcohol, lauryl alcohol, phenol, benzyl alcohol, hydroquinone, catechol, resorcinol, ethylene glycol, neopentyl glycol, 1,4-cyclohexanedimethanol, and diethylene glycol.
 10. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer is selected from the group consisting of aliphatic polyesters comprising C₂₋₁₀ diacid residues and C₂₋₁₀ diol residues; wherein said C₂₋₁₀ diacid residue is at least one selected from the group consisting of malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, and sebacic acid.
 11. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer comprises diol residues; wherein said diol residues is at least one of the following C₂-C₁₀ diols: ethylene glycol, diethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,2-butylene glycol, 1,3-butylene glycol, 1,4-butylene glycol, neopentyl glycol, 1,5-pentanediol, 1,6 hexanediol, 1,5-pentylene glycol, triethylene glycol, and tetraethylene glycol.
 12. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer is a polyglycol.
 13. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer comprises one or more of: A) from about 5 to about 95 weight % of a C₂-C₁₂ carbohydrate organic ester, wherein the carbohydrate comprises from about 1 to about 3 monosaccharide units; and B) from about 5 to about 95 weight % of a C₂-C₁₂ polyol ester, wherein the polyol is derived from a C₅ or C₆ carbohydrate.
 14. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer comprises at least one carbohydrate ester and said carbohydrate portion of the carbohydrate ester comprises an α-anomer, a β-anomeror a mixture thereof.
 15. The cellulose ester/elastomer composition according to claim 1 wherein said plasticizer is a solid, non-crystalline resin.
 16. The cellulose ester/elastomer composition according to claim 1 wherein said compatibilizer is a non-reactive compatibilizer; wherein said non-reactive compatibilizer contains a first segment that is compatible with said cellulose ester and a second segment that is compatible with said elastomer.
 17. The cellulose ester/elastomer composition according to claim 16 wherein said first segment is at least one oligomer or polymer selected from the group consisting of cellulose esters; cellulose ethers, polyoxyalkylenes, polyglycols, polyesters, polyacrylates, polymethacrylates, polyacetals, polyvinylpyrrolidone, polyvinyl acetate, and polyvinyl alcohol.
 18. The cellulose ester/elastomer composition according to claim 16 wherein said second segment is selected from the group consisting of polyolefins, polydienes, polyaromatics, and copolymers.
 19. The cellulose ester/elastomer composition according to claim 16 wherein said non-reactive compatibilizers are selected from the group consisting of ethoxylated alcohols, ethoxylated alkylphenols, ethoxylated fatty acids, block polymers of propylene oxide and ethylene oxide, polyglycerol esters, polysaccharide esters, and sorbitan esters.
 20. The cellulose ester/elastomer composition according to claim 1 wherein said compatibilizer is a reactive compatibilizer wherein said reactive compatibilizer has a hydrocarbon chain that is compatible with said elastomer and has at least one functional group capable of reacting with said cellulose ester.
 21. The cellulose ester/elastomer composition according to claim 20 wherein said reactive compatibilizer is selected from the group consisting of long chain fatty acids, long chain fatty acid chlorides, long chain fatty acid anhydrides, epoxidized oils and fatty esters, styrene maleic anhydride copolymers, maleic anhydride grafted polypropylene, copolymers of maleic anhydride with olefins and/or acrylic esters, and copolymers of glycidyl methacrylate with olefins and/or acrylic esters.
 22. The cellulose ester/elastomer composition according to claim 1 wherein said reactive compatibilizer has a polar chain that is compatible with said cellulose ester and also has at least one functional group capable of reacting with said elastomer.
 23. The cellulose ester/elastomer composition according to claim 22 wherein said reactive compatibilizer is selected from the group consisting of cellulose esters and polyethylene glycols.
 24. A cellulose ester/elastomer composition according to claim 1 wherein said non-polar elastomer is at least one selected from the group consisting of natural rubber, polybutadiene, polyisoprene, styrene-butadiene rubber, polyolefins, ethylene propylene diene monomer (EPDM), and polynorbornene.
 25. An article produced from the cellulose ester/elastomer composition of claim
 1. 